Technical Data Sheet Type: Pearlthane? D11H92S is a polycaprolactone copolyester-based thermoplastic polyurethane. Excellent flow and mechanical properties and an outstanding low compression set value and high temperature resistance. Main application: Injection Moulding See reverse side for processing information * Based on moulded plaques Listed values are “typical (average) values” and should /cannot be applied for specification purposes Physical Properties Value (Metric) Unit Test Method Hardness A/3: 92- D/3: 46 Shore A/D ISO 868 Specific Gravity 1.15 g/cm3 ISO 2781 Tensile Strength 47 MPa ISO 527-2/5A/500 Ultimate Elongation 511 % ISO 527-2/5A/500 Tensile Stress at: - 100 % Elongation 8 MPa ISO 527-2/5A/500 - 300 % Elongation 17 MPa ISO 527-2/5A/500 Compression Set: - 70h / 23?C 13 % ASTM 395B - 22h / 70?C 19 % ASTM 395B - 70h / 100?C 37 % ASTM 395B Tear Strength nicked 125 kN/m ISO 34-1B Abrasion Resistance 20 mm3 ISO 4649-A Vicat Softening Point Annealed 139 Unannealed 133 ?C ISO 306 (A50)